Sugarcane bagasse ash as a potential quartz replacement in red ceramic

Autores: Rainho Teixeira, S.R.|Souza, A E. de|Almeida Santos, G.T. de|Vilche Peña, A.F.|Gil Miguel, A.
Fuente: J. Am. Ceram. Soc.
en prensa
2008

Sugarcane bagasse ash (SCBA) is an industrial waste that contains silicon and aluminum oxides as the major components and iron, calcium, magnesium, and potassium oxides as the main minor components. In this paper, SCBA from one Brazilian factory was characterized and tested for its influence on the ceramic properties of clay/ash ceramic probes. Prismatic probes were pressed (18 MPa) using a ceramic mass mixed with 0%, 5%, 8%, and 10% ash. The probes were fired at temperatures between 800° and 1200°C. X-ray diffraction, X-ray fluorescence, thermal analysis (differential thermal analysis, thermogravimetric analysis/differential thermogravimetric analysis), and tests for texture (particle-size analysis), flexural strength, and linear shrinkage were carried out to characterize the samples. The results showed that the amount of ash to be incorporated will depend on mainly the composition of clay but also ash, and indicated that the clay used in this work can incorporate up to 10% weight of ash to produce solid bricks. The results also showed an improvement in ceramic/ash properties up to sintering temperatures higher than 1000°C.

Si desea obtener más información sobre este contenido contacte con nuestro Centro de Documentación

Regístrate para leer más