Autores: Levinson, R.|Berdahl, P.|Akbari, H.|Miller, W.|Joedicke, I.|Reilly, J.|Suzuki, Y.|Vondran, M.
Fuente: Solar energy materials and solar cells
91 (4), 304-314
We describe methods for creating solar-reflective nonwhite surfaces and their application to a wide variety of residential roofing materials, including metal, clay tile, concrete tile, wood, and asphalt shingle. Reflectance in the near-infrared (NIR) spectrum (0.7?2.5 µm) is maximized by coloring a topcoat with pigments that weakly absorb and (optionally) strongly backscatter NIR radiation, and by adding an NIR-reflective basecoat (e.g., one colored with titanium dioxide rutile white) if both the topcoat and the substrate weakly reflect NIR radiation. Coated steel and glazed clay-tile roofing products achieved NIR reflectances of up to 0.50 and 0.75, respectively, using only cool topcoats. Gray-cement concrete tiles achieved NIR reflectances as high as 0.60 with coatings colored by NIR-scattering pigments. Such tiles could attain NIR reflectances of up to 0.85 by overlaying a white basecoat with a topcoat colored by NIR-transparent organic pigments. Granule-surfaced asphalt shingles achieved NIR reflectances as high as 0.45 when the granules were covered with a white basecoat and a cool color topcoat.
Si desea obtener más información sobre este contenido contacte con nuestro Centro de Documentación
Regístrate para leer más